ASTM A234 WP91
化学成分和力学性能
化学成分 Chemical Compositions (max,%)
C Mn P S Si Cr Mo Ni Cu V
0.08-0.12 0.3-0.6 ≤0.02 ≤0.01 0.2-0.5 8-9.5 0.85-1.05 ≤0.4 --- 0.18-0.25
拉伸性能 Tensile Requirements
| 钢级Grade | WP91 |
| 抗拉强度范围Tensile strength, range ksi [MPa] | 85–110 [585–760] |
| 小屈服强度 Yield strength, min, ksi [MPa] (0.2 % offset or 0.5 % extension-under-load) | 60 [415] |
| WP9 CL1 & CL3 | WP9 CL1 & CL3 | |
| 伸长率 | 纵向 | 横向 |
| 标距为4D的标准圆形试样或小尺寸比例试样的小值 | 22 | 14 |
| 5/16 in.(7.94mm)及其以上壁厚的矩形试样,和所有在全截面下试验的小尺寸试样,标距为2in.(50mm) | 30 | 20 |
| 5/16 in.(7.94mm)以下壁厚的矩形试样, 标距为2in.(50mm)(试样宽1/2in.,12.7mm) | A | A |
| 壁 | 厚 | WP9 CL1 & CL3 | WP9 CL1 & CL3 |
| in. | [mm] | 纵向 | 横向 |
| 5⁄16 (0.312) | 7.94 | 30 | 20 |
| 9⁄32 (0.281) | 7.14 | 28.5 | 19 |
| 1⁄4 (0.250) | 6.35 | 27 | 18 |
| 7⁄32 (0.219) | 5.56 | 25.5 | … |
| 3⁄16 (0.188) | 4.76 | 24 | … |
| 5⁄32 (0.156) | 3.97 | 22.5 | … |
| 1⁄8 (0.125) | 3.17 | 21 | … |
| 3⁄32 (0.094) | 2.38 | 19.5 | … |
| 1⁄16 (0.062) | 1.59 | 18 |
上表列出了壁厚每减薄1⁄32 in. [0.79 mm]时小伸长率。壁厚处在上述两值之间时,小伸长率的值由下式确定:
| 实验方法 | 公式 |
| 纵向 | E= 48t + 15.00 |
| 横向 | E= 32t + 10.00 |
E = 标距2 in. 或[50 mm]的伸长率, %,
t = 试样的实际厚度, in. [mm].
硬度 Hardness – 高248HB
热处理:平顶山舞钢
除非采购方规定了ASTM A234 补充要求S1外,WP91管件做正火加回火热处理。正火温度范围为1040 °C-1080 °C,回火温度范围为730 °C-800 °C。